PC/ABS Toughen Flame Retardant Masterbatch (FR-PC/ABS803-T)

Price:
Negotiable
minimum:
Total supply:
Delivery term:
The date of payment from buyers deliver within days
seat:
Beijing
Validity to:
Long-term effective
Last update:
2017-07-21 11:14
Browse the number:
81

Send an inquiries

Company Profile

Suzhou Haixiang Plastic Chemical Co.,Ltd

By certification [File Integrity]

Contact：haixiang(Mr.)

Email：

Telephone：

Area：Beijing

Address：Yuanzhong Bridge West, Guangfu Town Industrial Zone, Wuzhong District, Suzhou, Jiangsu, China

Website：http://www.sz-flameretardant.com/ http://haixiang.shanxismy.com/

PRODUCT DETAILS

Introduction

HXFR-PC/ABS803-T consists of environment friendly flame retardant system of bromine, passed the evaluation of SGS, CTI etc. certification authority and comply with EU ROHS requirement. Advantages: good compatibility with PC/ABS, high effective, anti-yellowing, oxidative resistance, no mold corrosion, non-blooming, high smoothness and good low-temperature toughness.

Application

Mainly used in imported fire-retardant PC/ABS recycled material injection and modification. parts of computer, Electric meter, connecter, enclosure of notebook or mouse.

Index

Item	Index
Appearance	White Granular
Density g/cm³	1.42
Decomposition Temp ℃≥	300
Content %>	52
Water Content %≤	0.1
Recommended Dosage	100:10
Solubility Index g/min,200℃5kg	40
Melting Temp ℃≥	140

Extrusion Process (Twin Screw Extruder)

Note: Vacuum when production; Recommended Screw L/D 1:36-40;

Packing/Storage

25KG/bag: Transported as a common chemical and stored in dry and cool place, avoid direct sunlight.

Appendix：Application Examples

1-1.Formula

Materials	Formula A
Fire-retardant PC/ABS Recycling Materials	100
HXFR-PC/ABS803-T	10

1-2.Technical Data

Properties	Test Methods	Unit	Recycling Materials	Formula A
Density	ASTMD-792	g/cm³	1.2	1.22
Melt Index(200℃5KG)	ASTMD-955	g/10min	-	-
Tensile Strength	ASTM-D638	MPa	57.8	52.2
Elongation At Break	ASTM-D638	%	22.2	21.8
Flexural Strength	ASTM-D790	MPa	83.6	78
Flexural Modulus	ASTM-D790	MPa	2451.5	2297
Izod Impact Strength Notched(23℃)	ASTM-D256	KJ/m²	20.0	21.6
Flame Retardancy 1.6mm	UL94	‐‐	V1	V0
GWFI	IEC60695-2-12	℃	Not Pass	750pass

1-3. PC/ABS Injection Process:

Drying condition: Drying at 80-100 deg C to 2-3 hours by desiccant dryers.

Injection machine temperature setup:

Heating Zone	Step1	Step2	Step3	Nozzle
Temperature	225	230	240	235

All the application typical data above are just for reference, not an official warranty certificate.Provide different design solutions according to requirement of customers.