ABS High Performance Black Flame Retardant Masterbatch (FR-ABS300H)

Price:
Negotiable
minimum:
Total supply:
Delivery term:
The date of payment from buyers deliver within days
seat:
Beijing
Validity to:
Long-term effective
Last update:
2017-09-27 10:35
Browse the number:
430

Send an inquiries

Company Profile

Suzhou Haixiang Plastic Chemical Co.,Ltd

By certification [File Integrity]

Contact：haixiang(Mr.)

Email：

Telephone：

Area：Beijing

Address：Yuanzhong Bridge West, Guangfu Town Industrial Zone, Wuzhong District, Suzhou, Jiangsu, China

Website：http://www.sz-flameretardant.com/ http://haixiang.shanxismy.com/

PRODUCT DETAILS

Introduction

HXFR-ABS300 consists of environment friendly flame retardant system of bromine and antimony, passed the evaluation of SGS, CTI etc certification authority and comply with ROHS requirement. Advantage: high UV-Resistance, Non-blooming.

Application

Mainly used in black ABS injection and extrusion, such as: Panel, enclosure, frame of electric product and outer panel, Interior board, dashboard of automobile.

Index

Name	FR-ABS300H
Appearance	Black Granular
Content wt%>	74
Density g/cm³	2.0
Solubility Index g/min,200℃5kg	8.3
Decomposition Temp ℃≥	240
Water Content wt%≤	0.1
Melting Temp ℃≥	140

Extrusion Process (Twin Screw Extruder)

Note: Vacuum when production; Recommended Screw L/D 1:36-40.

Packing/Storage

25KG/bag: Transported as a common chemical and stored in dry and cool place, avoid direct sunlight.

Appendix：Application Examples

1-1.Formula

Materials	Formula A	Formula B	Formula C
Tianjin Dagu ABS417	78	80	75
HXFR-ABS300	22
HXFR-ABC302		20
HXFR-ABS303			25

1-2.Technical Data

Properties	Test Methods	Unit	ABS417	Formula A	Formula B	Formula C
Density	ASTMD-792	g/cm3	1.05	1.15	1.17	1.15
Melt Index	ASTMD-1238	g/10min	15.5
Tensile Strength	ASTM-D638	MPa	510	38.5	37.4	39.7
Elongation At Break	ASTM-D638	%	40	21.8	6.9	6.5
Flexural Strength	ASTM-D790	MPa	77	59.2	57.7	61.5
Flexural Modulus	ASTM-D790	MPa	25180	1900.4	2007.7	1875.3
Izod Impact Strength Notched(23℃)	ASTM-D256	KJ/m²	27	12.6	10.1	20.7
Flame Retardancy 3.2mm	UL94	‐‐	Non flame retardant	V0	V0	V0
CTI	IEC60695	GWFI:850/3.0	‐‐	Pass	Pass	Pass
Color			Natural color	Natural color	Natural color	Natural color

Note: the properties of HXFR-ABS300H are similar to HXFR-ABS300.

1-3. Injection Process:

Drying condition: Drying at 70-75 deg C to 2-3 hours by desiccant dryers.

Injection machine temperature setup:

Heating Zone	Step1	Step2	Step3	Nozzle
Temperature	205	210	220	200

All the application typical data above are just for reference, not an official warranty certificate. We provide different design solutions according to requirement of customers.